XRD patterns of stoichiometric ball‐milled samples annealed at different temperature and 1 hour holding time

XRD patterns of stoichiometric ball‐milled samples annealed at different temperature and 1 hour holding time

Source publication
XRD pattern of (A) stoichiometric mixture and (B) 20 hours ball milled...
(A) SEM image at 50 μm scale. (B) SEM image showing areas where EDS...
XRD patterns of stoichiometric ball‐milled samples annealed at...
Rietveld refinement results of XRD profile of ball‐milled sample...
+3 XRD of a ball‐milled sample annealed at 480°C at different holding times
Synthesis of Mg2Ni Using Stoichiometric and Superstoichiometric Compositions for Hydrogen Storage Applications
Article
Full-text available
  • Jul 2021
A Mg2Ni intermetallic compound was synthesized through a mechanochemical route using both stoichiometric and superstoichiometric mixtures of Mg and Ni. The former composition was processed by mechanical alloying, followed by annealing, while the latter composition using high-energy ball milling. X-ray diffraction (XRD) and Scanning electron microsc...
Cite
Download full-text

Similar publications

Figure 1. Real images of the samples (a) after cold compaction; (b)...
Figure 4. SEM of the two types of ball-milled powder: (a) represents...
Figure 6. TEM micrograph of ball-milled powder (Cu-5 wt% B-10 wt% Ti):...
Figure 7. TEM of two types of the composite after heat treatment: (a)...
+2 Figure 9. (a) DSC curve of the two types of alloy composite; (b) zoom...
Mechanical Alloying of Ball-Milled Cu-Ti-B Elemental Powder with the In Situ Formation of Titanium Diboride
Article
Full-text available
  • Dec 2022
This paper represents the fabrication and characterization (microstructural, mechanical, and electrical) of Cu-2wt% B-4 wt% Ti and Cu-5wt% B-10wt% Ti alloy from the ball-milled Cu, Ti, and B powders. The in situ formation of TiB2 was also discussed in the light of differential scanning calorimetry (DSC) and X-ray diffraction (XRD). This present wor...