A comparative investigation of gas sensing properties of SnO2 doped with WO3 based on thin film and bulk forms was achieved. Thin films were deposited by thermal evaporation technique on glass substrates. Bulk sensors in the shape of pellets were prepared by pressing SnO2:WO3 powder. The polycrystalline nature of the obtained films with tetragonal...
Context in source publication
Similar publications
In2O3 nanoparticle (NP)-decorated WO3 nanorods (NRs) were prepared using sol–gel and hydrothermal methods. The In2O3 NRs and WO3 NPs were crystalline. WO3 NP-decorated In2O3 NRs were also prepared using thermal evaporation and hydrothermal methods. The NO2 sensing performance of the In2O3 NP-decorated WO3 NR sensor toward NO2 was compared to that o...
This article is devoted to the investigation of the sensing behavior of chemically treated multi-walled carbon nanotubes (MWNTs) at room temperature. Chemical treatment of MWNTs was carried out with a solution of either sulfuric or chromic acids. The materials obtained were investigated by transmission electron microscopy, scanning electron microsc...
Tin oxide (SnO2) nanowires (NWs) and indium oxide (In2O3) nanoparticles (NPs) were synthesized using thermal evaporation and sol–gel methods, respectively. The NWs were decorated with the NPs by ultraviolet light irradiation and furnace annealing. The sensing properties of the NP-decorated NWs were compared with those of SnO2–In2O3 core–shell nanob...
Until now, SnO2 nanowires have been directly grown on alumina substrates with Au or Au-coated Pt electrodes by a thermal evaporation method using Sn or SnO2 powders under vacuum. However, in this study, SnO2 nanowires were successfully synthesized on the Pt phase of an alumina substrate by a thermal evaporation method using dibutyltin oxide [DBTO,...
Citations
In this study, crystalline SnO 2 -WO 3 nanocomposite thin films were grown through radio-frequency cosputtering of metallic Sn and ceramic WO 3 targets. The W content in the SnO 2 matrix was varied from 5.4 at% to 12.3 at% by changing the WO 3 sputtering power during thin-film growth. Structural analyses showed that increased WO 3 phase content in the nanocomposite films reduced the degree of crystallization of the SnO 2 matrix. Moreover, the size of the composite films' surface crystallites increased with WO 3 phase content, and the large surface crystallites were composed of numerous nanograins. Addition of WO 3 crystals to the SnO 2 matrix to form a composite film improved its light harvesting ability. The SnO 2 -WO 3 nanocomposite films exhibited improved photodegradation ability for Rhodamine B dyes compared with their individual constituents (i.e., SnO 2 and WO 3 thin films), which is attributable to the suitable type II band alignment between the SnO 2 and WO 3 . Moreover, an optimal WO 3 phase content (W content: 5.4 at%) in the SnO 2 matrix substantially enhanced the ethanol gas-sensing response of the SnO 2 thin film. This suggested that the heterojunctions at the SnO 2 /WO 3 interface regions in the nanocomposite film considerably affected its ethanol gas-sensing behavior.