Samples of tool steel 1.3343 (a) and carbon steel with paste (b), as well as quenching with HFC (c): 1 -sample; 2 -ceramic holder; 3 -sheath of paste; 4 -quartz chamber; 5 -protective shell; 6 -copper inductor tubes

Samples of tool steel 1.3343 (a) and carbon steel with paste (b), as well as quenching with HFC (c): 1 -sample; 2 -ceramic holder; 3 -sheath of paste; 4 -quartz chamber; 5 -protective shell; 6 -copper inductor tubes

Source publication
Cite
Download full-text

Context in source publication

Context 1
... heating was performed in the temperature range from 800-850 to 1200-1300 ºC. The samples of carbon steel were treated with paste and since their size was small, cooling of the samples in air with shell residues was considered to be the quenching process (Fig.1). ...

Similar publications

View
View
View
The chemical composition of the Pyrowear 53 (AMS 6308) steel
Microstructure and hardness of Pyrowear 53 steel after low-pressure vacuum carburizing at 921°C
Article
Full-text available
  • Nov 2020
The present paper studies and analyzes the low-pressure vacuum carburizing of Pyrowear 53 steel. The carburizing was performed at 921°C. The results after the completion of the treatment process are presented, i.e. microstructure of the surface layer and hardness. The results confirm that carburizing can be effectively used in hardening of the stee...